Химические и механические требования к углеродистой стали. ASTM A216 WCB
Jan 21, 2024
химические требования
| Element % | ||||||||||
| Material Grade | C | Mn | P | SB | Si | NiC | CrC | MoC | CuC | VC |
| WCB D J03002 | 0.30 | 1.00 | 0.035 | 0.035 | 0.60 | 0.50 | 0.50 | 0.20 | 0.30 | 0.03 |
1. All values are maximums.
2. For lower maximum sulfur content, see Supplementary Requirement S52
3. Specified Residual Elements- Except when Supplementary Requirement S50 is specified, the total content of these elements is 1.00 % maximum.
4. For each reduction of 0.01 % below the specified maximum carbon content, an increase of 0.04% manganese above the specified maximum will be permitted up to a maximum of 1.10 % for WCA.1.28 % for WCB and 1.40 % for WCC
Tensile Requirements
| Material Grade | Tensile Strength, ksi (MPa) | Yield Strength, ksi (MPa) | Elongation in 2 in.(50mm), % | Reduction of Area, % |
| WCB | 70-95 (485-655) | 36 (250) | 22 | 35 |
The equivalent material in forged type is ASTM A105N(refer to the standard accordingly).
Bosseal Valve is an experienced valve manufacturer of high-quality WCB casting valves, for any technical or commercial support please consider our teams at [email protected]
Cледующий: химические и механические требования к нержавеющей стали. astm a351 cf8m
Предыдущий: Сфера аттестации клапанов по ТАТ-MESC SPE 77-300 (2022)
Основанная в 2013 году, компания Bosseal является профессиональным производителем промышленной арматуры и располагается в городе Сучжоу, Китай. Мы специализируемся на проектировании и производстве шаровых, задвижных, глобоидных, обратных, дисковых, пробковых клапанов, а также трубопроводных фильтров‑грязевиков. Вся наша продукция изготавливается в строгом соответствии с международными стандартами, включая API, ASME, ISO, DIN, BS и EN. Уделяя особое внимание контролю качества и инженерному потенциалу, мы стремимся предоставлять надёжные и высокопроизводительные клапанные решения для промышленных применений по всему миру.